Cast C62400
Information
PRODUCT DESCRIPTION: Aluminum Bronze 11%
TEMPERS: HR50 Drawn and Stress Relieved
SOLIDS: 1/2" to 3" O.D.*
STANDARD LENGTHS: 144” *Consult mill for other sizes
Typical Uses
FASTENERS: nuts
INDUSTRIAL: bushings, cams, drift pins, gears, hydraulic bushings, support bushings, tie rods, valve balls, wear plates, welding wire
Similar or Equivalent Specification
CDA | ASTM | SAE | AMS | Federal | Military | Other |
---|---|---|---|---|---|---|
C62400 | B150 B150M | J461 J463 |
Chemical Composition
Cu%1 | Sn% | Fe% | Al% | Mn% | Si% |
---|---|---|---|---|---|
Rem. | 0.20 | 2.00-4.50 | 10.00-11.50 | 0.30 | 0.25 |
Chemical Composition according to ASTM B150/B150M-19
¹Cu value includes Ag
Note: Cu + Sum of Named Elements, 99.5% min. Single values represent maximums.
Machinability
Copper Alloy UNS No. | Machinability Rating | Density (lb / in³ at 68 °F) |
---|---|---|
C62400 | 50 | 0.269 |
Mechanical Properties
Mechanical Properties according to ASTM B150/B150M-19
HR50 Drawn and Stress Relieved Temper
Size Range: 1/2" and Under Rod
Tensile Strength, min | Yield Strength, at 0.5% Extension Under Load, min | Elongation, 4x Diameter or Specimen Thickness, min | Rockwell "B" Hardness | Remarks | ||
---|---|---|---|---|---|---|
ksi | MPa | ksi | MPa | % | min to max HRB | |
95 | 655 | 45 | 310 | 10 |
Size Range: Over 1/2" to 1" Rod Inclusive
Tensile Strength, min | Yield Strength, at 0.5% Extension Under Load, min | Elongation, 4x Diameter or Specimen Thickness, min | Rockwell "B" Hardness | Remarks | ||
---|---|---|---|---|---|---|
ksi | MPa | ksi | MPa | % | min to max HRB | |
95 | 655 | 45 | 310 | 10 |
Size Range: Over 1" to 2" Rod Inclusive
Tensile Strength, min | Yield Strength, at 0.5% Extension Under Load, min | Elongation, 4x Diameter or Specimen Thickness, min | Rockwell "B" Hardness | Remarks | ||
---|---|---|---|---|---|---|
ksi | MPa | ksi | MPa | % | min to max HRB | |
90 | 620 | 40 | 295 | 12 |
Size Range: Over 2" to 3" Rod Inclusive
Tensile Strength, min | Yield Strength, at 0.5% Extension Under Load, min | Elongation, 4x Diameter or Specimen Thickness, min | Rockwell "B" Hardness | Remarks | ||
---|---|---|---|---|---|---|
ksi | MPa | ksi | MPa | % | min to max HRB | |
90 | 620 | 40 | 275 | 12 |
Physical Properties
US Customary | Metric | |
---|---|---|
Melting Point - Liquidus | 1900 °F | 1038 °C |
Melting Point - Solidus | 1880 °F | 1027 °C |
Density | 0.269 lb/in³ at 68 °F | 7.45 gm/cm³ at 20 °C |
Specific Gravity | 7.45 | 7.45 |
Electrical Conductivity | 12% IACS at 68 °F | 0.07 MegaSiemens/cm at 20 °C |
Thermal Conductivity | 34 Btu/sq ft/ft hr/°F at 68 °F | 59 W/m at 20 °C |
Coefficient of Thermal Expansion 68-572 | 9 · 10-6 per °F (68-572 °F) | 15.6 · 10-6 per °C (20-300 °C) |
Specific Heat Capacity | 0.09 Btu/lb/°F at 68 °F | 377.1 J/kg at 20 °C |
Modulus of Elastic in Tension | 17000 ksi | 117212 MPa |
Modulus of Rigidity | 6400 ksi | 44127 MPa |
Fabrication Properties
Technique | Suitability |
---|---|
Soldering | Not Recommended |
Brazing | Fair |
Oxyacetylene Welding | Not Recommended |
Gas Shielded Arc Welding | Good |
Coated Metal Arc Welding | Good |
Spot Weld | Good |
Seam Weld | Good |
Butt Weld | Good |
Capacity for Being Cold Worked | Poor |
Capacity for Being Hot Formed | Excellent |
Forgeability Rating | 80 |
Machinability Rating | 50 |
Thermal Properties
Treatment | Minimum * | Maximum * |
---|---|---|
Annealing | 1100 | 1200 |
Hot Treatment | 1400 | 1625 |
* Temperature is measured in Fahrenheit