COPPER-BASED ALLOYS
C62410
CAST C62410
INFORMATION
PRODUCT DESCRIPTION: Aluminum Silicon Bronze
TEMPERS: HR50 Drawn and Stress Relieved
SOLIDS: 5/16" to 3" O.D.
HEX: 1/2" to 2" O.D.
RECTANGLES: Consult Mill
STANDARD LENGTHS: 144”
TYPICAL USES
ELECTRICAL: pole line hardware
INDUSTRIAL: bearings (high strength/corrosion resistant), bushings (aircraft), chemical process equipment, pickling equipment, valve bodies, valve stems
MARINE: bolts, lock washers, nuts, screws
SIMILAR OR EQUIVALENT SPECIFICATION
CDA
ASTM
SAE
AMS
Federal
Military
Other
C62410
B150 B150M
CHEMICAL COMPOSITION
Cu%1
Pb%
Sn%
Zn%
Fe%
Ni%2
Al%
Mn%
Si%
As%
Rem.
0.05
0.20
0.50
0.30
0.25
6.30-7.00
0.10
1.50-2.00
0.15
MACHINABILITY
Copper Alloy UNS No.
Machinability Rating
Density(lb / in 3 at 68 °F)
C62410
60
0.278
MECHANICAL PROPERTIES
Mechanical Properties according to ASTM B150/B150M-19

HR50 Drawn and Stress Relieved Temper
SIZE RANGE: UNDER 1/2" ROD AND BAR
Tensile Strength, min
Yield Strength, at 0.5% Extension Under Load, min
Elongation, 4x Diameter or Specimen Thickness, min
Rockwell "B" Hardness
Remarks
ksi
MPa
ksi
MPa
%
min to max HRB
90
620
45
310
9
80-100

SIZE RANGE: 1/2" TO 1" ROD AND BAR INCLUSIVE
Tensile Strength, min
Yield Strength, at 0.5% Extension Under Load, min
Elongation, in 4x Diameter or Specimen Thickness, min
Rockwell "B" Hardness
Remarks
ksi
MPa
ksi
MPa
%
min to max HRB
85
585
45
310
12
80-100

SIZE RANGE: OVER 2" TO 3" ROD AND BAR INCLUSIVE
Tensile Strength, min
Yield Strength, at 0.5% Extension Under Load, min
Elongation, in 4D, min
Rockwell "B" Hardness
Remarks
ksi
MPa
ksi
MPa
%
typical HRB
75
575
35
241
15
70-95

SIZE RANGE: OVER 3" TO 4" ROD AND BAR INCLUSIVE (M20 as hot rolled)
Tensile Strength, min
Yield Strength, at 0.5% Extension Under Load, min
Elongation, in 4D, min
Rockwell "B" Hardness
Remarks
ksi
MPa
ksi
MPa
%
typical HRB
70
483
30
207
15
65-95

SIZE RANGE: OVER 4" TO 6" ROD AND BAR (M30 as hot extruded)
Tensile Strength, min
Yield Strength, at 0.5% Extension Under Load, min
Elongation, in 4D, min
Rockwell "B" Hardness
Remarks
ksi
MPa
ksi
MPa
%
typical HRB
70
483
25
172
15
65-95

PHYSICAL PROPERTIES
US Customary
Metric
Density
0.278 lb/in3 at 68 °F
7.7 gm/cm3 at 20 °C
Specific Gravity
7.7
7.7